Wir verwenden Cookies, um für diese Website Funktionen wie z.B. Login, einen Warenkorb oder die Sprachwahl zu ermöglichen. Weiterhin nutzen wir für anonymisierte, statistische Auswertungen der Nutzung Google Analytics, welches Cookies setzt. Mehr Informationen finden Sie in unserer Datenschutzerklärung.
OK, ich bin einverstanden Ich möchte keine Google Analytics-Cookies
The International Journal of Oral & Maxillofacial Implants



Kennwort vergessen?


Int J Oral Maxillofac Implants 31 (2016), Nr. 6     22. Nov. 2016
Int J Oral Maxillofac Implants 31 (2016), Nr. 6  (22.11.2016)

Seite 1240-1246, doi:10.11607/jomi.4131, PubMed:27861648, Sprache: Englisch

Fracture Resistance of Straight and Angulated Zirconia Implant Abutments Supporting Anterior Three-Unit Lithium Disilicate Fixed Dental Prostheses
Saker, Samah / El-Shahat, Sameh / Ghazy, Mohamed
Purpose: The purpose of this study was to evaluate fracture resistance of straight and angulated zirconia implant abutments supporting anterior three-unit lithium disilicate fixed dental prostheses (FDPs).
Materials and Methods: Four different test groups (n = 8) representing anterior three-unit implant-supported allceramic FDPs were fabricated to fit an in vitro model with two implants. Groups 1 and 2 simulated a clinical situation with an ideal implant position for maxillary left central and right lateral incisors from a prosthetic point of view, which allowed for the use of a straight, prefabricated zirconia and titanium abutment. Groups 3 and 4 simulated a situation with a compromised implant position that required an angulated (15-degree) abutment. Tapered internal-connection implants (Direct's Legacy, 13-mm length, 3.7-mm diameter, Implant Direct) mounted in epoxy resin models were used in this study. Lithium disilicate (IPS e.max press, Ivoclar Vivadent) three-unit FDPs were fabricated and cemented using self-adhesive resin cement. The samples were subjected to thermocycling (2 × 3,000 × 5°C/55°C) and mechanical loading (TCML; 50 N × 600,000 cycles). Fracture resistances were determined for all the samples that survived aging. Kruskal-Wallis analysis of variance and Mann-Whitney U tests were performed to test for differences in fracture strength values at a 5% significance level.
Results: All samples subjected to TCML survived without mechanical failure. The highest fracture loads were associated with FDPs supported by implants with 0-degree abutment angulations compared with those FDPs supported by 15-degree abutment angulations (group 1: 538.7 ± 24.77 N; group 2: 542.17 ± 21.64 N; group 3: 523.57 ± 19.71 N; group 4: 528.37 ± 24.57 N). This difference in load-bearing capacity was not statistically significant (P > .05).
Conclusion: The use of angulated zirconia abutments for compensation of nonideal implant locations is possible without reducing the load-bearing capacity of implant-supported anterior three-unit lithium disilicate FDPs.

Schlagwörter: abutment angulations, all-ceramic FDPs, fracture resistance, zirconia abutment