Wir verwenden Cookies, um für diese Website Funktionen wie z.B. Login, einen Warenkorb oder die Sprachwahl zu ermöglichen. Weiterhin nutzen wir für anonymisierte, statistische Auswertungen der Nutzung Google Analytics, welches Cookies setzt. Mehr Informationen finden Sie in unserer Datenschutzerklärung.
OK, ich bin einverstanden Ich möchte keine Google Analytics-Cookies
The International Journal of Oral & Maxillofacial Implants



Kennwort vergessen?


Int J Oral Maxillofac Implants 34 (2019), Nr. 6     21. Nov. 2019
Int J Oral Maxillofac Implants 34 (2019), Nr. 6  (21.11.2019)

Seite 1404-1412, Sprache: Englisch

Bone Formation of Titanium Implant Surfaces Treated with Submicron Poly(lactide-co-glycolide)/ Recombinant Human Transforming Growth Factor-
Kim, Joohyung / Kim, Seong-Kyun / Heo, Seong-Joo / Koak, Jai-Young
Purpose: This study evaluated the effect of anodized titanium implants coated with submicron-sized poly(lactideco- glycolide) (PLGA)/recombinant human transforming growth factor-β2 (rhTGF-β2) particles via electrospray on osseointegration in an in vivo model.
Materials and Methods: An experimental group of anodized titanium implants coated with submicron PLGA/rhTGF-β2 particles by electrospray was compared topographically and histomorphometrically to noncoated anodized implants. Forty-eight anodized titanium implants were inserted into the tibias of 12 New Zealand rabbits. The histomorphometric specimens were prepared after sacrificing at 3 and 6 weeks after implant placement. Bone-to-implant contact percentage (BIC%) and bone area percentage (BA%) were calculated. The surface roughness and histomorphometric values were statistically analyzed, with a P value < .05 defined as statistically significant.
Results: The implant surfaces showed a uniform submicron-sized coating of PLGA/rhTGF-β2 particles. There was no significant difference in surface roughness between the groups. Both BIC% and BA% of the three best consecutive threads in the experimental group (3 weeks postplacement) were significantly higher than those of the control group (P = .045 and P = .048, respectively), whereas only the BIC% of the three best consecutive threads of the experimental group (6 weeks postplacement) was higher than that of the control group (P = .033). None of the groups tested showed any statistically significant differences in these metrics along the total length of the implant.
Conclusion: Within the limitations of this study, coating rhTGF-β2 on implants with the help of PLGA carriers by electrospray may have enhanced osseointegration during the early stage of implant healing period in in-vivo rabbit tibia model.

Schlagwörter: anodized implant, electrospray, osseointegration, polylactic acid-polyglycolic acid copolymer, recombinant human transforming growth factor-β2